Cabinet-Type Molten Iron Quality Management Test Machine for Furnace Front Furnace-Front Cabinet-Type Molten Iron Quality Tester

Main Technical Parameters

Measurement Name     Measurement Range      Measurement Accuracy

1. Temp                 0 - 1370℃               F.S±0.01%

2. CE%                  2.50% - 4.80%            ±0.08%

3. C%                   2.30% - 4.20%            ±0.05%

4. Si%                  0.60% - 3.80%            ±0.10%

5. SG%                  62% - 95%                ±10.0%

6. RM                   HT100 - HT350            Minimum Value

Software Functions

1. CE, C, and Si Content Measurement

(1) Can measure the active CE, C, and Si content of 10 target materials and calculate the cast iron grade (HT);

(2) Active CE carbon equivalent measurement range: 2.50 — 4.80%;

(3) Active C content measurement range: 2.30 — 4.20%;

(4) Active Si content measurement range: 0.60 — 3.80%;

(5) Correction values for active CE, C%, and Si% can be set within (-0.99 — +0.99).

2. Molten Iron Adjustment Calculation

Based on the target composition range, molten iron weight, carbon addition yield, silicon addition yield, and measurement results, the amount of carbon additive, ferrosilicon, or scrap steel required to achieve the target composition is calculated.

3. Spheroidization Rate Measurement

By measuring the eutectic degree and supercooling degree of the molten iron, the spheroidization rate of the spheroidal graphite cast iron can be calculated, provided that the active Mg content is sufficient.

4. Molten Iron Composition Management

Based on the product grade, the carbon equivalent, carbon content, and silicon content ranges are set. The instrument will display the content in different colors; unqualified values are displayed in red, and qualified values are displayed in green. Users can also modify the content ranges themselves.

5. Active Ingredient Measurement Screen Introduction

(1) Current Date and Time

(2) Instrument Version Number

(3) Maximum Temperature (TM)

(4) Primary Crystallization Temperature (TL)

(5) Eutectic Temperature (TE)

(6) Carbon Equivalent (CE1)

(7) Carbon Content (C%)

(8) Silicon Content (Si%)

(9) Carbon Equivalent and Range Graph (CE2)

(10) Carbon Content and Range Graph (C%)

(11) Silicon Content and Range Graph (Si%)

(12) Thermal Analysis Temperature Curve

(13) Real-time Temperature (Celsius)

(14) Current Detection Line Information Box

(15) Target Composition Range of Si

(16) "Function Switching" Button

(17) "Target Material" Button

(18) "Weight Setting" Button

(19) "Detection Setting" Button

(20) "Data Browsing" Button

(21) "End System" Button

6. Spheroidization Rate Measurement Interface Introduction

(1) Current Date and Time

(2) Instrument Version Number

(3) Maximum Temperature (TM)

(4) Primary Crystallization Temperature (TL)

(5) Eutectic Low Point (TEl)

(6) Recalescence Temperature (TEh)

(7) Cooling Rate and Chart

(8) Undercooling Degree and Chart

(9) Recalescence Time and Chart

(10) Spheroidization Rate and Chart

(11) Temperature Curve

(12) Real-time Temperature

(13) Current Detection Line Information

(14) "Function Switching" Button

(15) "Material Selection" Button

(16) "Weight Setting" Button (Invalid on this interface)

(17) "Detection Setting" Button

(18) "Data Browsing" Button

(19) "End System" Button

ACabinet-Type Molten Iron Quality Management Test Machine for Furnace Front Furnace-Front Cabinet-Type Molten Iron Quality Tester